Silicon Carbide Bulletproof Ceramics Sic Ceramics

• Port: Shanghai, China
• Transport Package: Cartons
• Payment Terms: L/C, T/T, D/P
• Refractoriness (℃): Refractoriness> 2000
• Feature: Long Time Materials
• Type: Refractory Material
• Shape: Customized
• Material: Silicon Carbide (SiC)
• Fracture Toughness: >4.5MPa.M1/2
• Elastic Modulus: 415gpa
• Bulk Density: >3.12g/cm3
• Bending Strength: >400MPa
• Thermal Conductivity: 148W.M-1.K-1
• Trademark: SANSHANTAOCI
• Origin: Yanhzhou, China

Sintered silicon carbide (SiC) ceramic is a new kind of bullet-proof ceramic material, with low density, high strength, high hardness, high temperature resistance, oxidation resistance, corrosion resistance and other excellent performances. Now it's the preferred general material for bulletproof ceramic pieces, mechanical seals, sand jets as well as magnetic pumps, shielding pump components, etc.
We produce sintered silicon carbide ceramics taking high purity sub-micron silicon carbide powder as raw material, according to the advanced formula imported from Japan, through the spray granulation, pressure molding and high temperature vacuum sintering. As the structure inside is compact, small grains, bullet-proof performance of this product is superior. The breast armor plates made of silicon carbide from our company have reached the standard NIJ0101.06III,IVand passed the grade IIIV bullet-tests held by National Bulletproof Equipment Testing Center for many times. Furthermore this product has successfully passed the target test certificated by the PLA. Nowadays the PLA troops are equipped with this ceramics composite armor.

The products specifications are as follows:

Product appearance	Quadrilateral pieces(mm)	Hexagonal Pieces (mm) (Across Flats)				whole plates with single-curved surface (mm)
Plane sizes	50*50	88	68	30	20	300*250
Thickness	5-20mm					6-10mm
Notes	Products can be produced according to customers' demands of particular sizes.

Performance Index:

Material	Bulk Density g/cm3	Bending Strength Mpa	Rockwell Hardness HRA	Thermal Conductivity W.m-1.K-1	Elastic Modulus GPa	Fracture Toughness Mpa.m1/2
Sintered Silicon Carbide	≥3.12	≥400	≥93	148	≥415	≥4.5